Beilstein J. Nanotechnol. 2016, 7, 474–483, doi:10.3762/bjnano.7.41
Figure 1: Concentration–depth profile in Ag(15 nm)/Au(15 nm) bilayer; as deposited and annealed at 170 °C.
Figure 2: Average concentration of Au and Ag inside the Ag (a) and Au (b) layers, respectively, versus the an...
Figure 3: Concentration–depth profile of a Ag(15 nm)/Pd(15 nm) bilayer; as deposited and annealed at 150 °C.
Figure 4: Comparison of depth profiles obtained after 8 h of heat treatment 150 °C. (a) Ag(15 nm)/Pd(15 nm)/s...
Figure 5: Saturation concentration of Pd and Ag inside the Ag and Pd layers, respectively, versus the anneali...
Figure 6: Depth profiles of Ag(15 nm)/Au(15 nm) (a) and Au(15 nm)/Ag(15 nm) (b) film systems after 20 h at 17...
Figure 7: XRD results (a) obtained by using Cu Kα radiation in θ–2θ mode on Ag(15 nm)/Pd(15 nm) after heat tr...
Figure 8: ln P (P = DAg/DAu) versus 1/T in the Ag/Au system.
Figure 9: Concentration–depth profile of Ag(27% Au)/Au(31% Ag) bilayer, (a) as-deposited, (b) annealed at 170...
Beilstein J. Nanotechnol. 2014, 5, 1491–1500, doi:10.3762/bjnano.5.162
Figure 1: Concentration profiles of Au(25nm)/Cu(50nm) system a) as deposited sample and annealed b) at 160 °C...
Figure 2: XRD θ–2θ patterns of Au(25nm)/Cu(50nm) samples a) as deposited, b) annealed at 180 °C for 5 h, c) f...
Figure 3: Concentration profiles of Au(10nm)/Cu(25nm) system a) as deposited and b) annealed at 180 °C for 5 ...
Figure 4: XRD θ–2θ patterns of Au(10nm)/Cu(25nm) annealed samples.
Figure 5: Concentration profiles of Au(25nm)/Cu(25nm) system a) as deposited sample and b) annealed samples.
Figure 6: XRD θ–2θ patterns of Au(25nm)/Cu(25nm) annealed samples.
Figure 7: Concentration profiles of Au(25nm)/Cu(12nm) system a) as deposited sample and b) annealed samples.
Figure 8: XRD θ–2θ patterns of Au(25nm)/Cu(12nm) annealed samples.
Figure 9: Bright field (top view) TEM images of Au(10nm)/Cu(15nm) bilayer a) as deposited and c) after 1 h of...
Figure 10: Dependence of the average concentration of elements on the annealing time at 150 °C in a) Au(25nm)/...